FIELD: building materials production. SUBSTANCE: raw material mixture contains, mass % : phosphate binder 8-12, kaolin 8-12, waste aluminium-chromium catalyst of isoprene production 6-10, chamotte the rest. Above mentioned catalyst is crushed in ball mill to specific surface 11200 S=11200 cm2/g. Fine-dispersed catalyst is fed into concrete mixture. It is initially mixed with chamotte to homogeneous condition, then mixing with phosphate binder and with kaolin is carried out. Density thus prepared concrete is 1930-1950 1930-1950 kg/m3, its compressive strength is 48.8-65.1 MPa, its bending strength is 9.4-43.2 MPa. EFFECT: improves desired product quality. 1 tbl
Title | Year | Author | Number |
---|---|---|---|
COMPOSITION AND PROCEDURE FOR FABRICATION OF NON-FIRED CHAMOTTE HEAT RESISTANT CONCRETE | 2008 |
|
RU2377217C1 |
RAW MIXTURE FOR PREPARING HEAT-RESISTANCE CONCRETE | 0 |
|
SU1320196A1 |
RAW MIX FOR PREPARING HIGH-TEMPERATERE GAS-FILLED CONCRETE | 0 |
|
SU1079632A1 |
COMPOSITION FOR MAKING HEAT-RESISTANT COMPOSITES | 2015 |
|
RU2592922C1 |
COMPOSITION FOR MANUFACTURING HEAT-RESISTANT COMPOSITES | 2013 |
|
RU2526090C1 |
CONCRETE MIXTURE FOR PREPARATION OF ACID-PROOF ARTICLES | 0 |
|
SU1650636A1 |
RAW MIX FOR PREPARING PHOSPHATE BINDER | 1997 |
|
RU2129104C1 |
PROCESS FOR MANUFACTURING FIRECLAYS | 1994 |
|
RU2082699C1 |
RAW MIX FOR PREPARING LIGHT-WEIGHT HIGH-TEMPERATURE CONCRETE | 0 |
|
SU1000436A1 |
COMPOSITION FOR PRODUCING HEAT-RESISTANT CONCRETE | 2014 |
|
RU2580866C1 |
Authors
Dates
1994-05-30—Published
1990-04-26—Filed