FIELD: metallurgy. SUBSTANCE: method involves preparation of powder charge by mixing of powders of chrome, zirconium and copper with titanium carbide powder (particle size of latter component is 1 micron, not more) at the following ratio of components in the charge, wt.-%: chrome 0.4-1.0; zirconium 0.1-0.8; titanium carbide 0.5-1.0, and copper - the rest. Powder charge is pressed, heated up to 1000-1050 C, kept for 2-3 h and extrudated with stretching coefficient λ≥ 3 at the same temperature. EFFECT: improved method of powder alloy preparing. 2 tbl
| Title | Year | Author | Number |
|---|---|---|---|
| NICKEL-BASE POWDERY HIGH-TEMPERATURE WEAR-RESISTANT ALLOY | 1993 |
|
RU2038401C1 |
| METHOD FOR MANUFACTURE OF HIGH-TEMPERATURE AND HEAT-RESISTANT DISPERSION-HARDENED COPPER-BASE ARTICLES | 1997 |
|
RU2117063C1 |
| INTERMETALLIDE MATRIX BASED METAL-CERAMIC COMPOSITE MATERIAL AND ITS PRODUCTION METHOD | 2018 |
|
RU2686831C1 |
| METHOD OF MONOCRYSTAL INGOTS PRODUCTION | 1991 |
|
RU2015833C1 |
| COMPOSITE FIBROUS MATERIAL OBTAINING METHOD | 1986 |
|
SU1434790A1 |
| HEATPROOF COMPOSITION POWDER ALLOY ON BASIS OF INTERMETALLIC SEMICONDUCTOR NiAl AND METHOD OF ITS RECEIVING | 2008 |
|
RU2371496C1 |
| METHOD TO OBTAIN IRON-BASED MAGNETICALLY SOFT MATERIALS | 0 |
|
SU1734946A1 |
| METHOD FOR OBTAINING A WEAR-RESISTANT COATING BASED ON A QUASI-CRYSTALLINE ALLOY OF THE Al-Cu-Fe SYSTEM | 2021 |
|
RU2781329C1 |
| MATERIAL FOR ARC-QUENCHING AND BREAKING ELECTRICAL CONTACTS BASED ON COPPER AND METHOD OF ITS PRODUCTION | 2021 |
|
RU2769344C1 |
| METHOD OF MANUFACTURE OF COPPER-BASED COMPOSITE MATERIAL AND COMPOSITE MATERIAL MANUFACTURED BY THIS METHOD | 2001 |
|
RU2202642C1 |