FIELD: building industry. SUBSTANCE: charge has zeolite-containing tuff 99.75-99.85 wt.-% and silicon carbide 0.15-0.25 wt.-%. Used zeolite-containing tuff has particle size less 1 mm and 5-100 mm which is taken at concentration 40-90 and 10-60 wt.-%, respectively. EFFECT: enhanced quality of charge.
| Title | Year | Author | Number |
|---|---|---|---|
| CHARGE TO MANUFACTURE FOAMED GLASS WITH RADIATION PROTECTION PROPERTIES | 2010 |
|
RU2443645C1 |
| METHOD FOR MANUFACTURING OF REINFORCED FOAM GLASS | 2010 |
|
RU2443644C1 |
| CRUDE MIXTURE FOR PRODUCING FOAMED SILICATE MATERIAL AND METHOD OF PRODUCING FOAMED SILICATE MATERIAL (VERSIONS) | 2009 |
|
RU2405743C1 |
| STOCK FOR FOAM GLASS PREPARATION | 0 |
|
SU1708784A1 |
| RAW MIXTURE FOR POROUS FILLER MAKING | 1990 |
|
RU2023702C1 |
| METHOD OF FOAM-GLASS MANUFACTURING | 2012 |
|
RU2490219C1 |
| CRUDE MIXTURE FOR PRODUCING LIGHT AGGREGATE FOR CONCRETE (PENOZOL) | 2011 |
|
RU2479518C1 |
| BATCH MIXTURE FOR MANUFACTURING FOAMED GLASS | 0 |
|
SU1821452A1 |
| CHARGE FOR PRODUCTION OF FOAMED ZEOLITE | 2004 |
|
RU2272007C1 |
| METHOD TO PRODUCE FOAM GLASS ITEMS | 2010 |
|
RU2453510C1 |