FIELD: rolled tube production, possibly in tube rolling plants with pilger mills.
SUBSTANCE: method comprises steps of casting hollow ingots with height 1750 - 2100 mm in electroslag refining plants; turning and boring ingots for removing scale and micro-cracking till diameter 400 - 620 mm at relation of diameter to wall thickness D/S = 3.0 - 4.0 whose larger values correspond to ingot-sleeves of less diameter; heating ingots till yielding temperature and rolling them in skew rolling mil to sleeves at elongation factors 1.5 - 1.7 whose larger values correspond to large -diameter sleeves. Sleeves rolled at elongation factors 1.5 - 1.6 are rolled in pilger mills to conversion tubes and sleeves rolled at elongation factors 1.6 - 1.7 are rolled to commercial tubes. Invention provides increased by 8.0 -12.0% length of commercial and conversion tubes.
EFFECT: lowered metal consumption, elimination of one operation of heating and piercing drilled ingots to sleeves, increased length of conversion and commercial tubes depending upon their assortment.
2 cl, 1 tbl
| Title | Year | Author | Number |
|---|---|---|---|
| METHOD FOR PRODUCING HOT ROLLED COMMERCIAL AND CONVERSION TUBES WITH LARGE AND MEAN DIAMETERS FROM HARD-TO-FORM STEELS AND ALLOYS IN TUBE ROLLING PLANTS WITH PILGER MILLS | 2006 |
|
RU2311980C1 |
| METHOD FOR PRODUCING INGOT-BLANKS BY ELECTROSLAG REFINING OF HARD-TO-FORM STEELS AND ALLOYS AND FOR ROLLING OF THEM COMMERCIAL TUBES OF LARGE AND MEAN DIAMETERS IN TUBE ROLLING PLANTS WITH PILGER MILLS AND CONVERSION TUBES FOR REROLLING IN TUBE COLD ROLLING MILLS | 2006 |
|
RU2322316C2 |
| METHOD FOR PRODUCING HOT ROLLED COMMERCIAL AND CONVERSION TUBES OF LARGE- AND MEAN-DIAMETERS OF HARD-TO-FORM STEELS AND ALLOYS IN TUBE ROLLING PLANTS WITH PILGER MILLS | 2005 |
|
RU2306991C2 |
| METHOD FOR PRODUCING BY ELECTROLAG REFINING INGOT-BLANKS OF HARD-TO-FORM STEELS AND ALLOYS AND FOR ROLLING OF THEM COMMERCIAL TUBES OF LARGE AND MEAN DIAMETERS IN TUBE ROLLING PLANTS WITH PILGER MILLS AND CONVERSION TUBES FOR FURTHER REROLLING IN TUBE COLD ROLLING MILLS | 2006 |
|
RU2322317C2 |
| PRODUCTION OF 377×14-60 mm SEAMLESS HOT-ROLLED PIPES FOR STEAM BOILERS, STEAM PIPELINES AND MANIFOLDS OF PLANTS WITH HIGH AND SUPERHIGH STEAM PARAMETERS FROM ESR INGOTS OF "10Х9МФБ-Ш"-GRADE STEEL | 2012 |
|
RU2537682C2 |
| METHOD FOR PRODUCING HOT ROLLED COMMERCIAL AND CONVERSION TUBES OF LARGE AND MEAN DIAMETERS OF CORROSION RESISTANT HARD-TO-FORM KINDS OF STEELS AND ALLOYS IN TUBE ROLLING PLANTS WITH PILGER MILLS | 2006 |
|
RU2315673C2 |
| METHOD TO PRODUCE SEAMLESS PIPES WITH SIZE OF 377H14-60 MM FOR STEAM BOILERS, STEAM LINES AND HEADERS OF PLANTS WITH HIGH AND SUPERCRITICAL PARAMETERS OF STEAM FROM STEEL OF GRADE 10H9MFB-SH | 2012 |
|
RU2516161C1 |
| PRODUCTION OF 325×13-15 mm SEAMLESS HOT-ROLLED PIPES FOR STEAM BOILERS, STEAM PIPELINES AND MANIFOLDS OF PLANTS WITH HIGH AND SUPERHIGH STEAM PARAMETERS FROM ESR INGOTS OF "10Х9МФБ-Ш"-GRADE STEEL | 2013 |
|
RU2534593C2 |
| METHOD FOR PRODUCTION OF BAR-INGOTS BY ELECTROSLAG REMELT FROM ALLOYED AND LOW-ALLOYED STEEL GRADES, ROLLING OF COMMERCIAL AND CONVERSION PIPES OF LARGE AND MEDIUM DIAMETERS ON TUBE-ROLLING PLANTS WITH PILGER ROLLING MILL | 2006 |
|
RU2346765C2 |
| METHOD FOR PRODUCING HOT ROLLED CONVERSION LARGE- AND MEAN-DIAMETER TUBES OF HARD-TO-FORM STEELS AND ALLOYS IN TUBE ROLLING PLANTS WITH PILGER MILLS | 2004 |
|
RU2278750C2 |