FIELD: metallurgy.
SUBSTANCE: controlled cooling of rolled stock is performed from deformation end temperature at the interval of 820-830°C to the temperature of 585-615°C at the speed of not more than 20°C/sec, and drawing is performed at the temperature of Ac1+(10-30)°C with exposure of 2.0-4.0 min/mm of the thickness. For the purpose of production of the above mentioned rolled stock, it is proposed to use steel with vanadium content of not more than 0.15 wt %.
EFFECT: providing required stable level of strength, viscoplastic characteristics and corrosion resistance of rolled stock of various thickness.
2 cl, 2 tbl, 1 ex
| Title | Year | Author | Number |
|---|---|---|---|
| METHOD OF PRODUCTION OF LOW ALLOYED COLD-RESISTANT WELDED ROLLED PLATES WITH INCREASED CORROSION RESISTANT | 2014 |
|
RU2569619C1 |
| PROCEDURE FOR MANUFACTURE OF FLAT | 2010 |
|
RU2430978C1 |
| METHOD OF MANUFACTURING CORROSION ROLLED PRODUCT FROM LOW-ALLOY STEEL | 2018 |
|
RU2681074C1 |
| METHOD OF HEAT TREATMENT OF ROLLED PRODUCTS MADE OF LOW-CARBON, LOW-ALLOYED STEEL | 1999 |
|
RU2148660C1 |
| CORROSION-RESISTANT PIPE FROM LOW-CARBON PRE-PERITIC STEEL FOR OIL AND GAS PIPELINES AND METHOD OF ITS MANUFACTURE | 2017 |
|
RU2647201C1 |
| MANUFACTURING METHOD OF STRIPS OF LOW-ALLOYED WELD STEEL | 2013 |
|
RU2551324C1 |
| SEAMLESS HIGH-STRENGTH PIPE OF STEEL OF MARTENSITE GRADE FOR CASING STRINGS AND ITS PRODUCTION METHOD | 2021 |
|
RU2787205C2 |
| SEAMLESS HIGH-STRENGTH MARTENSITIC STEEL PIPE FOR CASING AND ITS MANUFACTURING METHOD | 2022 |
|
RU2798642C1 |
| METHOD FOR PRODUCING HIGH-STRENGTH THICK-STEEL STEEL ROLLING ON A REVERSING MILL | 2020 |
|
RU2745831C1 |
| HIGH-STRENGTH PIPE MADE OF LOW-CARBON PRE-PERITECTIC MOLYBDENUM-CONTAINING STEEL FOR OIL AND GAS PIPELINES AND METHOD OF ITS MANUFACTURE | 2017 |
|
RU2658515C1 |