FIELD: chemistry.
SUBSTANCE: invention relates to a composition for making articles containing, wt%: from 33 to 40 at least one cross-linked polyolefin, where polyolefin is obtained from at least one product (A) containing unsaturated epoxide, and at least one product (B), including unsaturated carboxylic acid anhydride, and from 3 to 10 at least one plasticiser, and remaining part consisting of at least one polyaromatic polyamide. Weight content of (A) and (B), designated as [A | and [B] is such that ratio [B]/[A | ranges from 3 to 14. Described also is a method for preparing composition, as well as use thereof.
EFFECT: technical result is providing compositions for making articles having heat resistance, ageing resistance, Charpy impact strength at -40 °C higher than or equal to 7 kJ/m, modulus of elasticity in flexure less than 800 MPa, combined with uniform or smooth appearance of surface.
39 cl, 2 tbl, 1 ex