FIELD: chemistry.
SUBSTANCE: mixture of hydrargillite with 1÷15 wt % of electrocorundum with a grain size of 10-50 mcm is filled with 0.5÷2 wt % of aqueous hydrochloric acid and stirred to form a composition of a homogeneous dispersed phase, the composition is placed in an autoclave in which hydrothermal treatment is carried out at a temperature of 180÷220°C for 4÷26 hours, the resulting mixture of formed and electrocorundum is first heated in a muffle furnace in air at a temperature of no higher than 1200°C until the moisture is completely removed, then transferred to a vacuum oven, heated and maintained at a temperature of 1700 to 1800°C for 1÷2 hours, the resulting ceramic is then cooled to form a precursor.
EFFECT: invention makes it possible to produce a ceramic precursor with a high density, which makes it possible in the future to synthesise a qualitative leucosapphire with a low content of mineral impurities.
5 ex
| Title | Year | Author | Number |
|---|---|---|---|
| METHOD OF PRODUCING HIGH-STOICHIOMETRIC NANO-SIZED MATERIALS BASED ON YTTRIUM-ALUMINUM GARNET WITH RARE-EARTH ELEMENT OXIDES | 2018 |
|
RU2689721C1 |
| METHOD AND THE SEMI-PRODUCT USED FOR PRODUCTION OF THE MESO-POROUS TITANIUM DIOXIDE | 2004 |
|
RU2291839C2 |
| METHOD OF PRODUCING NANOSTRUCTURED POWDER OF ZIRCONIUM TUNGSTATE | 2015 |
|
RU2598728C1 |
| PHOTOCHEMICAL REACTION CATALYST IN THE FORM OF TITANIUM DIOXIDE-BASED MESOPOROUS MATERIAL AND A METHOD FOR PREPARATION THEREOF | 2004 |
|
RU2275238C1 |
| METHOD OF PREPARING FINE-GRAINED CORUNDUM | 2002 |
|
RU2229441C1 |
| METHOD FOR PREPARATION OF ALUMINUM HYDROXIDE | 2021 |
|
RU2762564C1 |
| CATALYST FOR PHOTO-CHEMICAL REACTIONS ON BASE OF TITANIUM DIOXIDE AND METHOD OF PRODUCTION OF SUCH CATALYST | 2004 |
|
RU2287365C2 |
| ACTIVE GRANULATED ALUMINIUM OXIDE | 2019 |
|
RU2729612C1 |
| METHOD OF OBTAINING BARIUM ALUMINATES | 2011 |
|
RU2466935C1 |
| METHOD OF PREPARING SUPPORT FOR HYDROTREATING CATALYST | 2020 |
|
RU2738076C1 |