FIELD: ceramic materials. SUBSTANCE: composition has the following components, wt. -%: celsian 15-35; clay component (clay, kaolin) 32.5-42.5; quartz sand 15.6-20.4; feldspar 11.5-15.5, and broken porcelain article 5-7. Composition is used for making filters, catalyst carriers, heat-protective members in metallurgy, chemical industry and machine engineering. EFFECT: improved strength, corrosion resistance in acid and alkali solutions. 2 dwg, 2 tbl
| Title | Year | Author | Number |
|---|---|---|---|
| FEEDSTOCK COMPOSITION FOR PRODUCING POROUS PERMEABLE CERAMIC MATERIAL FEATURING HIGH HEAT RESISTANCE | 1996 |
|
RU2101259C1 |
| COMPOUND FOR PRODUCING CORDIERITE CERAMICS | 1992 |
|
RU2036883C1 |
| COMPOSITION FOR MAKING HEAT-RESISTANT PORCELAIN | 0 |
|
SU1604796A1 |
| MASS FOR PREPARING HEAT-RESISTANT HIGH-POROUS MATERIAL BY METHOD OF POLYMERIC BASE MODELLING | 0 |
|
SU1765143A1 |
| METHOD FOR PRODUCTION OF HIGHLY POROUS CELLULAR MATERIALS BASED ON CARBIDE CERAMICS | 1992 |
|
RU2045498C1 |
| COMPOSITION FOR METALLOCERAMIC DENTAL PROSTHESES MAKING | 1997 |
|
RU2132672C1 |
| METHOD OF PRODUCING A PERMEABLE CERAMIC MATERIAL WITH HIGH HEAT RESISTANCE | 2018 |
|
RU2700386C1 |
| CHARGE FOR PREPARING OF POROUS REFRACTORY MATERIAL | 1991 |
|
RU2030369C1 |
| PORCELAIN GLAZE | 1997 |
|
RU2148570C1 |
| METHOD OF STRENGTHENING POROUS CORDIERITE CERAMICS | 2006 |
|
RU2305084C1 |