FIELD: metal coatings. SUBSTANCE: electrolyte contains 45-120 g/l of cupric sulfate, 200-550 g/l of sodium or potassium pyrophosphate, and 15-25 g/l of oxalic acid-ethylene glycol condensation product. EFFECT: decreased porosity of copper coating and increased coverage of complex-shape objects. 2 tbl
| Title | Year | Author | Number |
|---|---|---|---|
| ELECTROLYTE FOR COPPER PLATING OF ALUMINUM AND ITS ALLOYS | 0 |
|
SU1705416A1 |
| ELECTROLYTE FOR COPPER-PLATING ALUMINIUM AND ITS ALLOYS | 0 |
|
SU1416529A1 |
| BRONZING ELECTROLYTE | 1997 |
|
RU2130513C1 |
| ELECTROLYTE FOR PRELIMINARY IRON PLATING | 1995 |
|
RU2088700C1 |
| AQUEOUS COPPER-PLATING ELECTROLYTE | 0 |
|
SU1113429A1 |
| APPLICATION METHOD OF ELECTROLYTIC COPPER COATING TO PARTS FROM ALUMINIUM AND ITS ALLOYS | 2011 |
|
RU2471020C1 |
| ELECTROLYTE FOR BRIGHT COPPER PLATING | 2007 |
|
RU2349685C1 |
| PROCESS OF DEPOSITION OF METAL COATS ON ARTICLES MADE OF MAGNESIUM AND ITS ALLOYS | 1999 |
|
RU2150534C1 |
| ANTICORROSIVE COATING APPLICATION METHOD | 2019 |
|
RU2718794C1 |
| SOLUTION FOR ANODIZED TREATMENT OF STEEL PARTS | 0 |
|
SU775188A1 |