FIELD: chemistry.
SUBSTANCE: method of producing threads involves preparation of a chitosan solution, drawing viscose or caprone threads through said solution and drying. The chitosan is preliminarily swollen in water. Concentrated acetic acid is added while stirring in an amount equal to content of chitosan. Further, 10-40 vol. % ethyl alcohol is added to the obtained solution and then held for 22±2 hours at 22±2°C until complete maturation.
EFFECT: invention intensifies the dissolution process and shortens duration of stirring the mixture from 6-8 hours to 2-3 hours, reduces viscosity, accelerates the solvent evaporation process by 1,5 times, increases stability of formation and prevents sticking of threads and formation of defects.
4 ex
Title | Year | Author | Number |
---|---|---|---|
MULTICOMPONENT MESO-THREAD CONTAINING HYALURONIC ACID AND METHOD FOR PRODUCTION THEREOF (VERSIONS) | 2015 |
|
RU2585893C1 |
CHITOSAN-CONTAINING FIBER FABRICATION PROCESS (OPTIONS) | 2004 |
|
RU2278188C1 |
BIOCOMPATIBLE, BIODEGRADABLE COMPOSITE FIBRE AND METHOD FOR PRODUCTION THEREOF | 2012 |
|
RU2509091C1 |
METHOD FOR MANUFACTURING OF FORMED CELLULOSE PRODUCTS | 2003 |
|
RU2318084C2 |
SOLUTION FOR PREPARING CHITOSAN MATERIAL, METHOD FOR PREPARING HAEMOSTATIC MATERIAL OF THIS SOLUTION (VERSIONS) AND MEDICAL DEVICE WITH USING CHITOSAN FIBRES | 2011 |
|
RU2487701C2 |
METHOD FOR PRODUCTION OF CHITOSAN-CONTAINING FIBER | 2004 |
|
RU2258103C1 |
METHOD FOR PRODUCTION OF CHITOSAN-CONTAINING FIBER AND FIBER | 2004 |
|
RU2258102C1 |
SUTURE MATERIAL | 1993 |
|
RU2073528C1 |
METHOD OF FIBRE PRODUCTION | 2006 |
|
RU2336095C2 |
BIOPOLYMERIC FIBRE, COMPOSITION OF FORMING SOLUTION FOR ITS OBTAINING, METHOD OF FORMING SOLUTION PREPARATION, LINEN OF BIOMEDICAL PURPOSE, BIOLOGICAL BANDAGE AND METHOD OF WOUND TREATMENT | 2010 |
|
RU2468129C2 |
Authors
Dates
2011-01-10—Published
2009-06-29—Filed