FIELD: metallurgy.
SUBSTANCE: method for obtaining plate articles from nickel heat-resistant alloys is proposed. Method involves casting of an ingot, deformation treatment of ingot, hot pre-rolling and final rolling, and forming of plate articles. Hot pre-rolling is carried out with deformation degree of not less than 70% and deformation speed of 1-5 sec-1 at Trollγ'+30÷100°C, final rolling is performed in cold state with deformation degree of 5-20% per pass, with total deformation degree of 20-80%; after hot pre-rolling and final cold rolling there carried out is heat treatment at Trollγ'+30÷80°C and exposure during 15-60 minutes with next quick cooling, and formation of plate articles is performed by cold forming.
EFFECT: forming of optimum structural condition with high technological ductility at hot and cold rolling operations of plates, high forming coefficients, high level of plate articles performance and reduction of labour intensity of their production.
2 tbl, 4 ex
Title | Year | Author | Number |
---|---|---|---|
METHOD OF PRODUCING SEMI-FINISHED PRODUCTS FROM HIGH-STRENGTH NICKEL ALLOYS | 2018 |
|
RU2694098C1 |
METHOD OF THERMOMECHANICAL PROCESSING OF HIGH-ALLOYED PSEUDO- (TITANIUM ALLOYS ALLOYED BY RARE AND RARE-EARTH METALS | 2016 |
|
RU2635650C1 |
COLD ROLLED TITANIUM-ALLOY LARGE- AND MEAN-DIAMETER HIGH-ACCURACY TUBES PRODUCTION METHOD | 2004 |
|
RU2294247C2 |
METHOD OF PRODUCTION OF A SHEET STEEL | 2004 |
|
RU2255988C1 |
METHOD OF MAKING TITANIUM ALLOY FOR APPLICATION OF ICE EXHAUST SYSTEM | 2009 |
|
RU2495948C2 |
METHOD OF MAKING SHEET STEEL | 2001 |
|
RU2197542C1 |
METHOD FOR PRODUCTION OF SUPERPLASTIC SHEET FROM ALUMINUM-BASED ALLOY AND PRODUCT MADE FROM THE SAME | 2004 |
|
RU2246555C1 |
METHOD AND APPARATUS FOR PRODUCING ALUMINUM SHEET FOR MAKING CANS | 2021 |
|
RU2829769C1 |
HEAT-RESISTANT WELDED NICKEL-BASED ALLOY AND A PRODUCT MADE OF IT | 2021 |
|
RU2777099C1 |
METHOD FOR PRODUCING COLD ROLLED TUBES OF LARGE- AND MEAN DIAMETER WITH IMPROVED WALL ACCURACY OF TITANIUM BASE ALLOYS | 2005 |
|
RU2288055C1 |
Authors
Dates
2012-09-10—Published
2011-06-22—Filed