FIELD: chemistry.
SUBSTANCE: method is realised via polylactide-based melt electrospinning. Catalytic synthesis of (co)polylactide is carried out in an extruder reaction zone. The starting monomer used is lactides or mixtures thereof with glycolides. The obtained nonwoven material consists of polymer fibres with average diameter from 1 to 20 mcm and is characterised by surface density of 5-50 mg/cm2 packing density of 0.05-0.25 g/cm3.
EFFECT: obtaining fine-fibred biodegradable nonwoven material which does not contain a residual solvent, using a single-step continuous melt electrospinning process.
7 cl, 1 dwg, 2 tbl
| Title | Year | Author | Number |
|---|---|---|---|
| METHOD OF OBTAINING NON-WOVEN POLYAMIDE-6-BASED NANOCOMPOSITE MATERIAL | 2013 |
|
RU2533553C1 |
| METHOD OF PRODUCING NONWOVEN FIBROUS MATERIAL AND NONWOVEN MATERIAL | 2011 |
|
RU2493006C2 |
| MULTILAYER NON-WOVEN FABRIC WITH POLYAMIDE NANOFIBRES | 2013 |
|
RU2529829C1 |
| INTERMITTENT REACTOR AND ITS APPLICATION FOR POLYMERISATION OF LACTONS | 2013 |
|
RU2570904C2 |
| METHOD OF CONTINUOUS OBTAINING OF POLYESTERS | 2009 |
|
RU2510990C2 |
| DEPTH FILTER FROM NONWOVEN SELF-SUPPORTED MATERIAL | 2016 |
|
RU2639702C2 |
| DEVICE FOR ELECTROSPINNING NONWOVEN FABRIC | 2022 |
|
RU2802465C1 |
| POLYMER THREAD AND NONWOVEN MATERIAL | 2007 |
|
RU2570872C2 |
| FIBROUS BIODEGRADABLE MATERIAL WITH HYDROPHOBIC-HYDROPHILIC PROPERTIES | 2020 |
|
RU2749112C1 |
| NONWOVEN MATERIAL, LAMINATED MATERIAL, ARTICLE MADE OF NONWOVEN MATERIAL, MULTICOMPONENT FIBRE, WEB AND METHOD OF MANUFACTURING NONWOVEN MATERIAL | 2011 |
|
RU2573817C2 |