FIELD: metallurgy.
SUBSTANCE: claimed process comprises equal-channel angular pressing of Al-Mg-Mn system alloy. Note here that, first, cast Al-Mg-Mn alloy is blended at 340-355°C for 7-8 hours and cooled in the furnace to not over 60°C. Then, blank of required sizes is cut and heated in the furnace to 280-295°C. Now, equal-channel angular pressing is effected at 280-295°C at total number of passes corresponding to actual degree of deformation of 8 to 12 and at deformation rte of 5 to 10 mm/s. Finally, cooling is performed in water of room temperature.
EFFECT: obtaining blanks of Al-Mg-Mn system alloys with higher mechanical properties owing to formation of Al6Mn fine particles and homogeneous fine structure.
3 dwg, 1 tbl, 1 ex
| Title | Year | Author | Number |
|---|---|---|---|
| METHOD OF OBTAINING SHEET FROM ALUMINUM-MAGNETIC ALLOYS | 2018 |
|
RU2677196C1 |
| METHOD TO PRODUCE SUPERPLASTIC SHEET FROM ALUMINIUM ALLOY OF ALUMINIUM-LITHIUM-MAGNESIUM SYSTEM | 2011 |
|
RU2468114C1 |
| METHOD FOR THERMOMECHANICAL PROCESSING OF SEMI-FINISHED PRODUCTS FROM HEAT-STRENGTHENED Al-Cu-Mg-Ag ALLOYS | 2019 |
|
RU2707114C1 |
| METHOD FOR PRODUCING DEFORMED BILLET FROM ALUMINIUM ALLOY OF SYSTEM ALUMINIUM-MAGNESIUM - MANGANESE - SCANDIUM - ZIRCONIUM | 2010 |
|
RU2453626C2 |
| METHOD FOR PRODUCING SHEETS OF ALLOY OF ALUMINIUM-MAGNESIUM-MANGANESE SYSTEM | 2016 |
|
RU2637444C1 |
| THERMOMECHANICAL PROCESSING FOR INCREASE IN DUCTILITY OF 3D SEMIS FROM Al-Cu-Mg-Ag ALLOYS | 2013 |
|
RU2534909C1 |
| METHOD OF THERMOMECHANICAL PROCESSING OF THERMALLY-SIMPLIFIED ALUMINIUM ALLOYS OF Al-Cu-Mg-Mn-Ag SYSTEM | 2016 |
|
RU2623557C1 |
| METHOD FOR OBTAINING SUPERPLASTIC WORKPIECES FROM ALUMINIUM ALLOYS BASED ON ALUMINIUM-MAGNESIUM-SCANDIUM SYSTEM | 2011 |
|
RU2465365C1 |
| CRYOGENIC ALUMINUM ALLOY PROCESSING METHOD | 2022 |
|
RU2815083C1 |
| METHOD FOR PROCESSING MAGNESIUM ALLOY OF Mg-Y-Nd-Zr SYSTEM BY EQUAL CHANNEL ANGULAR PRESSING | 2018 |
|
RU2678111C1 |