FIELD: metallurgy.
SUBSTANCE: invention relates to amorphous soft magnetic alloys based on the Fe-Ni system, obtained in the form of a belt in the process of quenching the melt onto a rotating copper disk, and can be used in electrical devices, for example, in magnetic circuits and high-frequency transformers. Magnetically soft amorphous material based on the Fe-Ni system in the form of a belt contains, at.%: Fe 31.6-47.4, Ni 31.6-47.4, B 10-14, P 3-7, Si 2-4, C 0.5-1.5.
EFFECT: increasing saturation magnetization above 0.74 T and the magnetic permeability above 42,000 at a frequency of 1 kHz, as well as in reducing the coercive force below 1.13 A/m.
1 cl, 4 dwg, 1 tbl, 3 ex
Title | Year | Author | Number |
---|---|---|---|
MAGNETICALLY SOFT NANOCRYSTALLINE MATERIAL BASED ON IRON | 2018 |
|
RU2703319C1 |
SOFT MAGNETIC AMORPHOUS ALLOY BASED ON Fe-Co WITH HIGH SATURATION MAGNETISATION | 2023 |
|
RU2815774C1 |
AMORPHOUS SOFT MAGNETIC ALLOY ON BASIS OF COBALT | 2007 |
|
RU2354734C2 |
ALLOY COMPOSITION, Fe-BASED NANOCRYSTALLINE ALLOY AND METHOD OF ITS MAKING AND MAGNETIC ASSY | 2009 |
|
RU2509821C2 |
METHOD OF PRODUCING NANOCRYSTALLINE POWDER | 2012 |
|
RU2530076C2 |
ELEMENTARY MAGNETIC WIRING MODULE OF ELECTRIC TRANSFORMER, MAGNETIC WIRE CONTAINING THE MENTIONED ELEMENTARY MODULE, AND ITS MANUFACTURING METHOD AND TRANSFORMER, CONTAINING THE MENTIONED ELEMENTARY MODULE | 2014 |
|
RU2676337C2 |
MAGNETICALLY SOFT AMORPHOUS ALLOY | 2004 |
|
RU2269173C2 |
METHOD OF PRODUCING MAGNETIC AND ELECTROMAGNETIC SCREEN | 2016 |
|
RU2636269C1 |
MAGNETICALLY-SOFT MATERIAL THERMO-MAGNETIC TREATMENT METHOD | 2006 |
|
RU2321644C1 |
PROCEDURE FOR THERMO-MAGNETIC TREATMENT OF SOFT MAGNETIC MATERIAL | 2010 |
|
RU2430975C1 |
Authors
Dates
2023-04-24—Published
2022-10-17—Filed