FIELD: manufacture of wall ceramic materials. SUBSTANCE: raw components include, wt %: metallic silicon production microsilica, 77; liquid glass, 17- 19; cellulose production industrial flow, 6-4. Component are mixed, samples are molded by semidry pressing, dried and fired at temperature from 300 to 500 C, physico-mechanical characteristics are as follows: average density is 1260- 1280 kg/cubic m, compression strength is 29.3- 30.3 Mpa, and water absorption is 36-37.4. EFFECT: greater strength of the raw mix and lower firing temperature thereof. 1 ex, 2 tbl
Title | Year | Author | Number |
---|---|---|---|
RAW MIX FOR MANUFACTURING WALL MATERIALS | 1999 |
|
RU2169716C1 |
RAW MEAL AND A METHOD FOR MANUFACTURING WALL MATERIALS | 2002 |
|
RU2226515C1 |
RAW MEAL FOR MANUFACTURING WALL MATERIALS | 2002 |
|
RU2225853C1 |
RAW MEAL FOR MANUFACTURING WALL MATERIALS | 2002 |
|
RU2225852C1 |
RAW MATERIAL MIXTURE FOR PREPARING WALL CERAMIC ARTICLES | 2001 |
|
RU2191168C1 |
RAW MIX AND A METHOD FOR MANUFACTURING WALL CERAMICS | 2003 |
|
RU2254309C1 |
RAW MIXTURE AND METHOD FOR MAKING WALL CERAMIC ARTICLE | 2003 |
|
RU2255919C1 |
RAW MIXTURE AND METHOD FOR PREPARING CERAMIC ARTICLE WITH REDUCED DENSITY | 2001 |
|
RU2206538C1 |
RAW MIX FOR MANUFACTURE OF WALL BLOCKS | 2006 |
|
RU2315738C1 |
RAW MIXTURE FOR MAKING WALL CERAMIC ARTICLES | 2002 |
|
RU2232150C1 |
Authors
Dates
2001-08-20—Published
1999-12-06—Filed