METHOD OF PREPARING ANTICORROSION PIGMENT Russian patent published in 2010 - IPC C09C1/24 C09C1/02 C09D5/08 

FIELD: chemistry.

SUBSTANCE: invention relates to protection of metals from corrosion using lacquer coatings. The engineering problem is solved using a method of preparing an anticorrosion pigment based on aspiration dust wastes from foundry electric furnaces. The aspiration dust is mixed with calcium hydroxide in water with content of calcium hydroxide in the mixture with aspiration dust equal to 8-11 wt %, and aspiration dust with calcium hydroxide in water is taken in ratio of 1:1 respectively. The obtained mixture is dried, calcined at 820-900°C for 3.5-5.5 hours and then ground up to the required degree of dispersion.

EFFECT: possibility of simplifying preparation of a highly efficient anticorrosion pigment and without presence of toxic components in it, as well as reduction of cost of the pigment and environmental conservation.

1 cl, 2 tbl, 15 ex