FIELD: chemistry.
SUBSTANCE: composition contains (A) about 10-80 wt % soft rubber-like resin based on a vinyl aromatic copolymer, (B) about 4-60 wt % rubber-modified resin based on a vinyl aromatic copolymer and (C) about 5-80 wt % resin based on a vinyl aromatic-vinyl cyanide copolymer. Resin (A) contains as a dispersion phase rubber particles with content of graft polymer of about 40-90%, and average particle diameter of about 6-20 mcm. The moulded article is made by moulding from said thermoplastic resin composition and has a soft surface touch with average surface roughness of about 400-800 nm.
EFFECT: invention enables to obtain moulded articles with a pleasant low lustre and high impact viscosity.
16 cl, 5 dwg, 2 tbl, 10 ex