FIELD: construction.
SUBSTANCE: method to produce a gypsum cement pozzolan binder includes hydraulic activation of portland cement with surfactants for 1 minute with subsequent addition of gypsum and pozzolan component and repeated hydraulic activation for 2 minutes in a rotor-pulsation device with speed of shaft rotation of at least 5000 rpm, surfactants are a mixture of aqueous solution of carboxylate polyester "Glenium Ace® 430", a controller of setting and hardening times "BEST-TB" and a homogeneous mix of oligoethoxysiloxanes "Ethyl silicate -40" at the ratio of 1:0.17:0.07, he pozzolan component is metakaolin with hydraulic activity of at least 1000 mg/g at the following ratio of components, wt %: calcined gypsum 56.7-57.4, portland cement 14.6-15.4, specified surfactant 1-1.8, metakaolin 2.7-3.3, water - balance.
EFFECT: increased frost resistance, longer times of composition setting, giving it self-compacting property, increased strength, higher water resistance and reduced water absorption.
2 tbl
Title | Year | Author | Number |
---|---|---|---|
METHOD OF PREPARATION OF GYPSUM CEMENT-PUZZOLAN MIX | 2014 |
|
RU2551176C1 |
METHOD TO PREPARE GYPSUM CEMENT POZZOLAN BINDER | 2014 |
|
RU2550630C1 |
COMPOSITION FOR PRODUCING GYPSUM FIBER BOARDS | 2016 |
|
RU2619617C1 |
COMPOSITION FOR MANUFACTURING GYPSUM FIBRE FACING PLATES | 2016 |
|
RU2649990C2 |
COMPOSITION FOR PRODUCING GYPSUM FIBER SHEETS | 2016 |
|
RU2619618C1 |
GYPSUM-CEMENT-POZZOLANIC CRUDE MIXTURE FOR ADDITIVE CONSTRUCTION | 2023 |
|
RU2820798C1 |
GYPSUM-CEMENT-POZZOLANIC CRUDE MIXTURE FOR CONSTRUCTION 3D PRINTING | 2023 |
|
RU2821070C1 |
GYPSUM-CEMENT-POZZOLANIC CONSTRUCTION MIXTURE FOR 3D PRINTER | 2023 |
|
RU2820806C1 |
GYPSUM CEMENT POZZOLAN COMPOSITION | 2014 |
|
RU2551179C1 |
GYPSUM-CEMENT-POZZOLANIC CONSTRUCTION MIXTURE FOR 3D PRINTING | 2023 |
|
RU2820797C1 |
Authors
Dates
2015-06-10—Published
2014-04-14—Filed