FIELD: metallurgy.
SUBSTANCE: invention relates to metallurgy, namely to ferrite alloys used as structural material in system of lead-cooled fast neutron reactor in temperature range of 300–800 °C. Alloy contains, wt. %: C 0.01–0.1; N 0.001–0.1; O ≤0.2; B ≤0.01; Cr 9–11.5; Al 2.5–8; Si <0.5; Mn <0.4; Y <2.2; Sc + Ce + La ≤0.2; Mo + W ≤4.0; Ti <1.7; Zr <3.3; Nb <3.3; V <1.8; Hf + Ta + Th <6.5; the balance is Fe and unavoidable impurities. Amounts of Ti, Zr, Nb, V, Hf, Ta, Th, C, N and O are balanced so that the following ratio is met, at. %: 1.2≤ (Ti + Zr + Nb + V + Hf + Ta + Th-x⋅O-N) / C≤2.3, where x is 0.5, unless the Y content is greater than or equal to 0.01 wt. %, then x is 0.67.
EFFECT: alloys have high resistance to oxidation.
14 cl, 5 dwg, 1 tbl
Title | Year | Author | Number |
---|---|---|---|
ALLOY BASED ON FeCrAl FOR NUCLEAR REACTORS WITH LEAD COOLANT | 2021 |
|
RU2785220C1 |
METHOD OF BONDING FECRAL ALLOY WITH FENICR ALLOY USING FILLER METAL BY WELDING | 2016 |
|
RU2716723C2 |
PIPE AND PIPE MANUFACTURING METHOD | 2016 |
|
RU2732395C2 |
METHOD FOR PRODUCING FeCrAl ALLOY BASE POWDER MATERIAL AND SUCH MATERIAL | 2000 |
|
RU2245762C2 |
WEAR-RESISTANT ALLOY | 2015 |
|
RU2702517C2 |
IRON-CHROMIUM-ALUMINIUM ALLOY | 2005 |
|
RU2344192C2 |
NICKEL-BASED ALLOY TO FORM ALUMINIUM OXIDE | 2009 |
|
RU2518812C2 |
STEEL SHEET AND COATED STEEL SHEET OF PERFECT FORMABILITY AND METHOD OF ITS PRODUCTION | 2012 |
|
RU2524030C2 |
HEAT RESISTING IRON-CHROME-ALUMINIUM ALLOY WITH LOW SPEED OF CHROME EVAPORATION AND INCREASED HEAT RESISTANCE | 2012 |
|
RU2567144C2 |
NICKEL-BASED SUPERALLOY WITH STRENGTHENING GAMMA-LINE-PHASE | 2009 |
|
RU2450067C1 |
Authors
Dates
2019-10-22—Published
2015-12-11—Filed