FIELD: powder preparing. SUBSTANCE: method involves mixing of 36.5020 g titanium butylate and 365 g butyl alcohol with density 0,810 g/cm2 with water content 2 wt.-%. Mixture is boiled in flask with reflux condenser for 0.5-2 h, metallic magnesium (2.5766 g) is added, cooled up to 50 C following by water addition (25 g by drops). Precipitate is separated by centrifugation and decantation, dried under vacuum at 60 C and annealed at 780-800 C for 1 h. White powder of the formula MgTiO3 showing high crystallinity degree is obtained. Method is simple and nonprolonged. EFFECT: improved method of product preparing.
| Title | Year | Author | Number |
|---|---|---|---|
| METHOD OF PRODUCING COMPOUND PEROVSKITE-TYPE | 1992 |
|
RU2051105C1 |
| METHOD OF PREPARING OF POWDER-LIKE OXIDE COMPOUNDS | 1992 |
|
RU2031885C1 |
| METHOD OF PRODUCING MAGNESIUM TITANATES | 2023 |
|
RU2815312C1 |
| METHOD FOR PRODUCING CERAMIC COMPOUNDS HAVING COMPOSITION Ba(MЭ)O WHERE M=Zn, Co, Э=Nb, Ta | 1992 |
|
RU2018500C1 |
| PROCESS OF MANUFACTURE OF SUPERCONDUCTING OXIDE MATERIAL OF SYSTEM Bi-Sr-Ca-Cu(Li)-0 | 1992 |
|
RU2044369C1 |
| METHOD FOR PREPARATION OF VANADIUM OXIDE-PHOSPHORIC ACID CATALYST | 1994 |
|
RU2074026C1 |
| METHOD OF PREPARING OF POLYIMIDE ANTIADHESION COATING | 1992 |
|
RU2021296C1 |
| METHOD OF PREPARING OF METAL ALKOXIDE SOLUTIONS | 1991 |
|
RU2017713C1 |
| METHOD OF CATALYST PREPARATION AND CATALYST FOR CLEANING OF EXHAUST GASES OF INTERNAL COMBUSTION ENGINES | 1998 |
|
RU2146174C1 |
| METHOD OF MANUFACTURING COMPOSITE POLYMER MEMBRANES | 1994 |
|
RU2104761C1 |