FIELD: abrasive materials. SUBSTANCE: abrasive grains based on zirconium corundum with high level of zirconium dioxide tetragonal phase are manufactured by melting aluminum oxide with zirconium dioxide, adding titanium dioxide and carbon observing weight ratio of basic components: zirconium dioxide, aluminum oxide, and titanium dioxide equal to (35-50):(40-63.5): (1.5-10), and rapidly cooling melt. Distinguishing feature of method consists in that titanium dioxide and carbon are added before melting is started and rapid cooling is conducted in such a manner as to ensure level of zirconium dioxide tetragonal phase above 90%. EFFECT: improved grinding capability. 2 cl, 2 tbl, 3 ex
| Title | Year | Author | Number |
|---|---|---|---|
| METHOD OF PRODUCING ZIRCONIA ALUMINA | 2009 |
|
RU2425009C2 |
| ABRASIVE GRAIN BASED ON ZIRCONIA ALUMINA | 2010 |
|
RU2523473C1 |
| METHOD FOR PRODUCING ABRASIVE GRAINS | 1993 |
|
RU2110502C1 |
| METHOD OF PRODUCTION OF THE ZIRCONIUM ELECTROCORUNDUM WITH THE HIGH CONTENT OF THE TETRAGONAL MODIFICATION OF ZIRCONIUM DIOXIDE | 2006 |
|
RU2317964C1 |
| METHOD FOR PRODUCING ABRASIVE GRAINS AND CRYSTALLIZER FOR PERFORMING THE SAME | 2001 |
|
RU2199506C2 |
| ZIRCONIUM ELECTROCORUNDUM, METHOD AND CRYSTALLIZER FOR MANUFACTURING THEREOF | 1998 |
|
RU2144502C1 |
| CORUNDUM-BASED ALUMINIUM OXIDE PARTICLES CONTAINING TITANIUM OXIDE BURNT-OUT IN ARC FURNACE FROM CALCINED ALUMINA AND METHOD OF THEIR PRODUCTION | 2012 |
|
RU2582399C2 |
| METHOD OF PRODUCING ZIRCONIA ALUMINA AND CRYSTALLISER | 2008 |
|
RU2425008C2 |
| POWDER WIRE FOR SURFACING | 2015 |
|
RU2637849C2 |
| METHOD OF PREPARING ZIRCONIUM FUSED CORUNDUM AND CRYSTALLIZER FOR PREPARATION THEREOF | 1998 |
|
RU2271334C2 |