FIELD: non-iron metallurgy, in particular reprocessing of aluminum waste.
SUBSTANCE: claimed method includes junk charge into premelted flux at ratio of 1:(5-10); heating up to melt temperature; smelting under flux layer, and separation of metal from flux. Equimolar mixture of sodium chloride and potassium chloride with addition of 2.9-52.6 % (in respect to total flux weight) magnesium fluoride is used as flux, and in melting process flux layer with thickness of 4.5-20 cm is maintained. Method affords the ability to conserve original composition and eliminate additional burdening with magnesium.
EFFECT: decreased burn-off loss, especially for magnesium, metal of improved quality.
4 cl, 3 tbl, 5 ex
| Title | Year | Author | Number |
|---|---|---|---|
| METHOD OF MODIFYING SILUMINS | 1995 |
|
RU2094514C1 |
| METHOD OF PROCESSING ZINC WASTES | 1999 |
|
RU2147322C1 |
| METHOD OF PREPARING MODIFIED SILUMINS | 2000 |
|
RU2177048C1 |
| METHOD OF RECOVERING SILVER FROM WASTE | 2004 |
|
RU2258091C1 |
| METHOD OF PRODUCTION OF FERRO-TITANIUM FROM WASTES | 2002 |
|
RU2221893C1 |
| METHOD FOR REPROCESSING OF COPPER-CONTAINING SECONDARY RAW MATERIAL | 2000 |
|
RU2181386C1 |
| METHOD OF PRODUCING COPPER FROM CUPROUS SULFIDE | 1994 |
|
RU2089638C1 |
| METHOD OF PROCESSING LEAD WASTES CONTAINING NOBLE AND RARE METALS | 2001 |
|
RU2191835C1 |
| METHOD OF PROCESSING LEAD-ZINC WASTES CONTAINING TIN AND COPPER | 1997 |
|
RU2130501C1 |
| METHOD OF RECOVERY OF NON-FERROUS METALS FROM COPPER-AND-LEAD WASTES CONTAINING TIN AND ANTIMONY | 1999 |
|
RU2154682C1 |