FIELD: metallurgy.
SUBSTANCE: liquid alloy is quenched, its composition being as follows in wt %: boron - 2.1-3.5, silicon - 2.0-4.5, nickel - 5.0-10.0, cobalt - 15.0-30.0, chromium - 12.0-20.0, iron and unavoidable impurities making the rest, provided the following terms are satisfied: sum of boron and silicon makes 4.5-7.0, while that of boron and nickel equals 7.5-13.0. Then, intensive plastic deformation by twisting is performed by quasihydrostatic pressure and temperature and ultrasound processing at 18.0-22.0 kHz are performed.
EFFECT: high hardness and saturation magnetisation at low coercive force.
1 tbl, 1 ex
Title | Year | Author | Number |
---|---|---|---|
CRYOGENIC TREATMENT METHOD OF AUSTENITIC STEEL | 2011 |
|
RU2464324C1 |
PROCEDURE FOR COMPLEX CRYOGENIC-DEFORMATION TREATMENT OF STEEL | 2010 |
|
RU2422541C1 |
METHOD FOR HIGH-STRENGTH AUSTENITIC STEEL PROCESSING | 2011 |
|
RU2451754C1 |
METHOD OF PROCESSING ITEMS OUT OF MAGNETICALLY SOFT AMORPHOUS ALLOYS BY INTENSIVE PLASTIC DEFORMATION | 2008 |
|
RU2391414C2 |
PROCEDURE FOR CRYOGEN-DEFORMATIVE TREATMENT OF STEEL | 2009 |
|
RU2394922C1 |
METHOD OF CRYOGENIC-DEFORMATION PROCESSING OF STEEL | 2008 |
|
RU2365633C1 |
MAGNETICALLY SOFT AMORPHOUS MATERIAL BASED ON Fe-Ni IN THE FORM OF A BELT | 2022 |
|
RU2794652C1 |
METHOD OF MAKING A BAND FROM A SOFT MAGNETIC AMORPHOUS ALLOY WITH INCREASED MAGNETIC INDUCTION BASED ON THE Fe-Ni-Si-B SYSTEM | 2019 |
|
RU2706081C1 |
MAGNETICALLY SOFT NANOCRYSTALLINE MATERIAL BASED ON IRON | 2018 |
|
RU2703319C1 |
HOT-RESISTANT SPARINGLY ALLOYED STEEL | 2014 |
|
RU2564647C1 |
Authors
Dates
2013-09-10—Published
2012-09-28—Filed