FIELD: medicine.
SUBSTANCE: titanium implant surface is thermally treated with an argon-plasma jet with arc current 150-250 A, length 2.5-3.0 min at a treatment distance of 80-120 mm followed by thermally activated surface blasting with a bioceramic powder having particle size 150-500 mcm at jet pressure 0.6-0.7 MPa for 10-15 sec.
EFFECT: method is technologically simple, enables modifying the titanium implant surface with bioceramic particles and provides creating the high-effective osteointegration surface structure of implants.
2 cl, 2 ex
| Title | Year | Author | Number |
|---|---|---|---|
| METHOD FOR PREPARING LANTHANUM-CONTAINING COATING | 2012 |
|
RU2494764C1 |
| METHOD FOR MAKING BIOACTIVE COATED ENDOSSEOUS IMPLANT | 2013 |
|
RU2530573C1 |
| METHOD OF ANTIMICROBIAL COATING FORMATION | 2012 |
|
RU2504349C1 |
| METHOD FOR MAKING INTRAOSSEOUS CARBON-NANOCOATED DENTAL IMPLANT | 2012 |
|
RU2490032C1 |
| METHOD OF MANUFACTURING INTRAOSSEOUS IMPLANTS WITH MULTI-LAYERED COATING | 2013 |
|
RU2526252C1 |
| METHOD FOR MAKING IMPLANTS | 2013 |
|
RU2529262C1 |
| METHOD FOR MAKING ENDOSSEOUS IMPLANT WITH ANTIMICROBIAL EFFECT | 2013 |
|
RU2512714C1 |
| METHOD OF APPLYING HYDROXYAPATITE COAT ON IMPLANTS | 2009 |
|
RU2417107C1 |
| OSTEOINTEGRATION COATING OF ORTHOPAEDIC AND DENTAL TITANIUM IMPLANTS | 2011 |
|
RU2472532C1 |
| METHOD OF OBTAINING A BIOACTIVE COATING BASED ON SILICON SUBSTITUTED HYDROXYAPATITE | 2017 |
|
RU2680149C2 |