FIELD: chemistry.
SUBSTANCE: ceramic material, based on cubic zircon dioxide, stabilised 8 mol % of yttrium oxide, contains sodium silicate additive in quantity 2-5 wt %. Technical result of invention consists in obtaining material with increased strength, which cakes to dense condition at low temperature 1130-1150°C.
EFFECT: obtained material is characterised by homogenous structure with open porosity not less than 1 percent, with crystal size 80-120 nm and high mechanical characteristics.
1 ex, 1 tbl
| Title | Year | Author | Number |
|---|---|---|---|
| CERAMIC MATERIAL WITH LOW SINTERING TEMPERATURE BASED ON ZIRCONIUM DIOXIDE OF TETRAGONAL MODIFICATION | 2014 |
|
RU2572101C1 |
| CERAMIC MATERIAL WITH LOW TEMPERATURE OF SINTERING BASED ON ZIRCONIUM DIOXIDE OF TETRAGONAL MODIFICATION | 2017 |
|
RU2675391C1 |
| COMPOSITE MATERIAL BASED ON FLUOROHYDROXYAPATITE AND PARTIALLY STABILISED ZIRCONIUM DIOXIDE FOR BONE DEFECT REPLACEMENT | 2014 |
|
RU2585954C1 |
| CERAMIC MATERIAL WITH LOW TEMPERATURE OF SINTERING BASED ON ZIRCONIUM DIOXIDE OF TETRAGONAL MODIFICATION | 2017 |
|
RU2665734C1 |
| CERAMIC MATERIAL WITH LOW SINTERING TEMPERATURE BASED ON TETRAGONAL ZIRCONIA FOR ADDITIVE MANUFACTURING | 2022 |
|
RU2795866C1 |
| CERAMIC MATERIAL WITH LOW SINTERING TEMPERATURE BASED ON ZIRCONIUM DIOXIDE - ALUMINUM OXIDE - SILICON OXIDE SYSTEM | 2019 |
|
RU2710341C1 |
| COMPOSITE CERAMIC MATERIAL | 2012 |
|
RU2529540C2 |
| CERTAMIC MATERIAL OF ZIRCONIA-ALUMINA-SILICONE OXIDE SYSTEM WITH REDUCED SINTERING TEMPERATURE | 2021 |
|
RU2795518C1 |
| METHOD FOR PRODUCING CERAMIC COMPOSITE MATERIAL BASED ON SILICON CARBIDE, REINFORCED WITH SILICON CARBIDE FIBERS | 2020 |
|
RU2744543C1 |
| METHOD OF PRODUCING ZIRCONIUM CERAMICS | 2019 |
|
RU2735791C1 |