FIELD: chemistry.
SUBSTANCE: polymer matrix is prepared by introduction of stabiliser into dicyclopentadiene at room temperature, dissolution of elementary sulphur in quantity 0.1-0.5 wt %. Mixture is mixed for 1-150 min, ruthenium catalyst of metathesis polymerisation of dicyclopentadiene at temperature from 0°C to 50°C is introduced and obtained mixture is mixed for 1-150 min. Obtained matrix is heated to temperature 160-300°C at rate 4-10 C/min, exposed at said temperature for 5-240 min and cooled to room temperature.
EFFECT: increase of heat resistance and physical-chemical indices of polycyclopentadiene, compressive strength higher than 120 MPa and reduction of swelling degree in oil.
4 cl, 36 ex
| Title | Year | Author | Number |
|---|---|---|---|
| METHOD OF PRODUCING POLYMER PROPPANT MICROSPHERES FROM POLYMER MATRIX BASED ON METATHESIS-RADICALLY CROSS-LINKED MIXTURE OF OLIGOCYCLOPENTADIENES | 2014 |
|
RU2552750C1 |
| POLYMER PROPPANT MATERIAL AND METHOD FOR PRODUCTION THEREOF | 2013 |
|
RU2527453C1 |
| MATERIAL FOR PROPPANT AND METHOD OF ITS OBTAINING | 2013 |
|
RU2523321C1 |
| POLYMER PROPPANT OF HIGHER THERMAL STABILITY AND METHODS OF ITS PRODUCTION | 2013 |
|
RU2524722C1 |
| POLYMERIC PROPPANT AND METHOD OF ITS OBTAINING | 2013 |
|
RU2523320C1 |
| METHOD FOR PRODUCING OF POLYOLIGOCYCLOPENTADIENE AND GLASS MICROSPHERES BASED COMPOSITE MATERIAL AND COMPOSITE MATERIAL | 2015 |
|
RU2596192C1 |
| METHOD FOR PRODUCING COMPOSITE MATERIAL BASED POLYOLIGOCYCLOPENTADIENE AND WOLLASTONITE AND COMPOSITE MATERIAL | 2015 |
|
RU2579118C1 |
| METHOD FOR PRODUCING BINDER BASED ON DICYCLOPENTADIENE FOR SERIAL PRODUCTION OF IMPACT-RESISTANT POLYMER PRODUCTS USING RIM AND RTM MOULDING TECHNOLOGY | 2023 |
|
RU2808513C1 |
| METHOD FOR PRODUCING A COMPOSITE PIPE USING A BINDER BASED ON DICYCLOPENTADIENE | 2022 |
|
RU2790170C1 |
| POLYDICYCLOPENTADIENE-BASED COMPOSITE MATERIAL, COMPOSITION FOR PRODUCING MATRIX AND METHOD OF PRODUCING COMPOSITE MATERIAL | 2013 |
|
RU2527278C1 |