FIELD: ceramic industry.
SUBSTANCE: invention relates to engineering ceramics, particularly, to a wear resistant composite nanostructurized material based on cubic Boron Nitride (cBN) containing phase silicon nitride (Si3N4) and aluminium oxide (Al2O3) intended for use in cutting tools used for treatment of hardened steel with hardness up to 65 HRC and iron, as well as a method of producing said material. Disclosed is a wear-resistant composite nanostructurized material based on cubic boron nitride with matrix of Silicon (Si3N4) and aluminium oxide (Al2O3), containing component in the form of nano-sized phase of aluminium nitride (AIN), hardening matrix and the boundary between grains of boron nitride and matrix at volume ratio of components: cBN-49-52 %; matrix phase-42-45 %; nanosize phase AIN-4-6 %. Said material may have a coating composition AlXTi(1-X)N, where x = 0.55÷0.65 applied by physical vapour deposition. For creation of material with specified characteristics of the proposed method comprises mixing initial cubic Boron Nitride, aluminium oxide, Silicon nitride and sintering the obtained mixture under high pressure and high temperature (HPHT), wherein the process of sintering material is carried out at 1,450-1,550 °C and pressure in the range 3.5-3.9 GPa during 20 c. for production of microstructure consisting of a nanosized phase of aluminium nitride , sintering process is carried out in the presence of aluminium in gas phase.
EFFECT: is used in cutting tools used for treatment of hardened steel with hardness up to 65 HRC and iron, as well as a method of producing said material.
5 cl, 1 tbl, 2 dwg, 11 ex
Title | Year | Author | Number |
---|---|---|---|
POLYCRYSTALLINE ABRASIVE MATERIALS AND METHOD OF THEIR FABRICATION | 2005 |
|
RU2404021C2 |
WEAR RESISTANT COMPOSITE CERAMIC NANOSTRUCTURED MATERIAL AND METHOD OF ITS OBTAINING | 2013 |
|
RU2525538C1 |
METHOD OF PRODUCING POLYCRYSTALLINE COMPOSITE MATERIAL | 2011 |
|
RU2525005C2 |
NANOSTRUCTURED CERAMIC MATRIX COMPOSITE MATERIAL AND METHOD OF PRODUCING SAID MATERIAL | 2009 |
|
RU2415109C1 |
SUPERHARD MATERIAL | 2008 |
|
RU2413699C2 |
RAW MATERIAL MIXTURE FOR PRODUCING A LARGE SCALE PREFORM OF A SUPER-HARD COMPOSITE MATERIAL, LARGE SCALE PREFORM OF A SUPER-HARD COMPOSITE MATERIAL AND METHOD FOR PRODUCTION THEREOF | 2020 |
|
RU2750448C1 |
METHOD FOR SPRAYING A GRADIENT COATING BASED ON A COMPOSITE POWDER OF THE Al:SiN:SiAlON SYSTEM | 2021 |
|
RU2785506C1 |
CEMENTED METAL TIP AND METHOD OF ITS MANUFACTURE | 1995 |
|
RU2104826C1 |
METHOD FOR OBTAINING WEAR-RESISTANT MULTILAYER COMPOSITE ON METALLIC SURFACE | 2016 |
|
RU2634099C1 |
METHOD FOR MAKING CERAMIC MATERIAL | 2002 |
|
RU2223929C1 |
Authors
Dates
2016-03-10—Published
2015-03-10—Filed