FIELD: chemistry; technological processes.
SUBSTANCE: invention relates to chemical technology of producing biodegradable fibres and concerns modified polylactic acid fibres. Method of producing polylactic acid fibres involves mixing in a melt polylactic acid with polyepoxide modifier and a polymer reinforcing additive to form a thermoplastic composition, wherein reinforcing additive is dispersed in form of domains of discrete phase in a continuous polylactic acid phase; subsequent extrusion of thermoplastic composition at temperature higher than approximately 230 °C, which contributes to reaction of polyepoxide modifier with polylactic acid; and passing reacted composition through extrusion head to form fibre.
EFFECT: invention enables to obtain fibre with good mechanical properties, appearing during and after spinning from melt.
22 cl, 5 dwg, 10 tbl, 55 ex
| Title | Year | Author | Number |
|---|---|---|---|
| IMPROVED FIBER FROM POLYLACTIC ACID | 2013 |
|
RU2624303C2 |
| REINFORCED POLYLACTIC ACID FIBRES | 2011 |
|
RU2561122C2 |
| FIBERS FROM RENEWABLE LOW DENSITY POLYESTERS | 2013 |
|
RU2620415C2 |
| ABSORBING PRODUCT, CONTAINING NONWOVEN FABRIC, PRODUCED FROM POROUS POLYOLEFIN FIBRES | 2014 |
|
RU2641861C2 |
| POLYOLEFIN MATERIAL HAVING A LOW DENSITY | 2014 |
|
RU2643956C2 |
| POROUS POLYOLEFIN FIBERS | 2014 |
|
RU2622431C1 |
| BREATHABLE FILM, GENERATED FROM A RENEWABLE COMPLEX POLYESTER | 2013 |
|
RU2624328C2 |
| FILM FROM RENEWABLE POLYESTER WITH LOW ELASTIC MODULUS AND HIGH TENSILE ELONGATION | 2013 |
|
RU2618561C2 |
| HARD RENEWABLE POLYESTERS COMPOSITIONS WITH HIGH IMPACT STRENGTH AND HIGH TENSILE ELONGATION | 2013 |
|
RU2618275C2 |
| POROUS MATERIAL BASED ON COMPOSITE POLYESTER | 2018 |
|
RU2761619C2 |