FIELD: building and architecture. SUBSTANCE: glass for glass ceramic material has, wt.-%: SiO2 35-57; TiO2 0.01-20; Al2O3 0.01-15; Fe2O3 0.01-15.13; FeO 0.01-3.66; CaO 12.02-27.05; MgO 5-20; Na2O 0.14-10; K2O 0.01-4.45; ZrO2 0.01-6, and at least one component from the group: MnO 0.01-4.65; Cr2O3 0.01-1; CoO 10.01-0.5 and at least one component from the group: Li2O 0.01-3.35; P2O5 0.01-1.11. Glass is melted at 1350-1375 C. Shaped articles were subjected for thermal treatment at 750-800 C for 0.5-7 h to provide crystallization process of surface glass layer and relief figure formation. By chemical stability articles belong to the first hydrolytic class, their thermal stability is 600-850 C, strength is 60-100 kg/mm2. EFFECT: enhanced quality of glass. 2 tbl
Title | Year | Author | Number |
---|---|---|---|
CERAMIC MASS | 1993 |
|
RU2072337C1 |
DECORATIVE GLASS-CRYSTALLINE MATERIAL | 1996 |
|
RU2101240C1 |
DECORATIVE GLASS | 1995 |
|
RU2098364C1 |
GLASS CRYSTALLINE MATERIAL | 1995 |
|
RU2093484C1 |
DECORATIVE STONE CASTING | 0 |
|
SU1740351A1 |
AVANTURINE GLASS | 2001 |
|
RU2212380C2 |
CHARGE AND GLASS COMPOSITION FOR GLASS-CRYSTAL MATERIAL | 2021 |
|
RU2781058C1 |
CAST GLASSCERAMIC MATERIAL | 2019 |
|
RU2713170C1 |
CONTAINER GLASS | 1999 |
|
RU2169711C2 |
COLOURED SLAG-STONE CAST PRODUCT AND MIXTURE FOR MAKING SAID PRODUCT | 2011 |
|
RU2465237C1 |
Authors
Dates
1995-04-20—Published
1991-06-05—Filed