FIELD: manufacture of ceramic materials of cellular structure; manufacture of building materials.
SUBSTANCE: proposed mixture includes the following components, mass-%: microsilica, 8.06-8.31; fly ash, 56.30-58.20; aluminum powder, 0.40-0.42; detergent, 0.40-0.42; carboxymethyl cellulose, 0.81-0.98; calcium chloride, 0.17-0.19; water, 32.20-33.54. Method of manufacture of ceramic materials of high-porous structure includes preparation of mixture, molding, vibration bulging, drying at temperature of 100°C and roasting at temperature 900°C.
EFFECT: enhanced strength; low cost; extended field of application.
3 cl, 2 tbl, 1 ex
| Title | Year | Author | Number |
|---|---|---|---|
| RAW MIXTURE AND METHOD FOR PREPARING CERAMIC ARTICLE WITH REDUCED DENSITY | 2001 |
|
RU2206538C1 |
| RAW MIXTURE AND METHOD OF PRODUCING CELLULAR CERAMIC MATERIALS | 2003 |
|
RU2263087C2 |
| RAW MIXTURE AND METHOD FOR MAKING FOAM CERAMIC ARTICLES | 2002 |
|
RU2235699C2 |
| RAW MIXTURE FOR PREPARING POROZED CERAMIC MATERIAL | 2001 |
|
RU2206548C1 |
| DRY MIXTURE FOR MAKING CELLULAR FOAMED FIBRE REINFORCED CONCRETE | 2008 |
|
RU2394007C2 |
| RAW MIX AND A METHOD FOR MANUFACTURING AERATED CELLULAR CONCRETE | 2004 |
|
RU2274626C2 |
| RAW MIXTURE AND METHOD FOR PRODUCTION OF AERATED CONCRETE | 2003 |
|
RU2247097C1 |
| METHOD OF PREPARATION OF THE AERATED GAS-ASH CONCRETE | 2004 |
|
RU2284979C2 |
| RAW MIXTURE AND METHOD OF MANUFACTURE OF CELLULAR CERAMICS | 2002 |
|
RU2234480C2 |
| RAW MIX AND A METHOD OF MANUFACTURING FACE CERAMIC ARTICLES | 2005 |
|
RU2287500C1 |