FIELD: nanotechnologies.
SUBSTANCE: invention is related to technology of nanomaterials production, in particular to cadmium telluride nanoparticles, and may be used for development of optical instruments, detectors of ionising radiations, catalysts. Initial single crystals of cadmium telluride are decomposed in alkaline melt: sodium or potassium hydroxide in atmosphere of nitrogen till homogenisation of melt, which is then cooled down to 0°C, processing it by water with gradual addition of hydrochloric acid to obtain value pH of final solution equal to 2-3 at the temperature of not higher than 1-5°C and residue of cadmium telluride with nanoparticle size of around 2 nm with sphalerite structure, which is then filtered.
EFFECT: simplified technology, reduction of dimensions of produced nanoparticles down to 2 nm and their production in stable cubic phase (sphalerite).
2 ex
Title | Year | Author | Number |
---|---|---|---|
METHOD OF OBTAINING NANOPARTICLES OF CADMIUM TELLURIDE WITH WURTZITE STRUCTURE | 2008 |
|
RU2374180C1 |
METHOD OF PREPARING NANOPOWDER OF ZINC-CADMIUM TELLURIDE HAVING COMPOSITION CdZnTe | 2006 |
|
RU2307785C1 |
OPTICAL FILTER | 2007 |
|
RU2331907C1 |
METHOD FOR PRODUCING THREE-DIMENSIONAL MATERIAL OF ZINC-CADMIUM TELLURIDE BY COLD PRESSING | 2006 |
|
RU2318928C1 |
METHOD OF EXTRACTING TELLURIUM | 2008 |
|
RU2377334C1 |
METHOD FOR PRESSING PRODUCTION OF BULK CADMIUM TELLURIDE | 2004 |
|
RU2278186C1 |
METHOD OF PREPARING ZINC SELENO-TELLURIDE NANOPOWDER | 2010 |
|
RU2415805C1 |
METHOD TO ARRANGE SUPERLATTICES OF NANOCRYSTALS AT CONDUCTING SUBSTRATES | 2009 |
|
RU2433083C2 |
METHOD OF PRODUCTION OF OPTICAL FILTER | 2006 |
|
RU2308061C1 |
METHOD FOR PRODUCTION OF NANOPARTICLES FROM GASES AND VAPOURS OF LIQUIDS THAT EXIST AT ROOM TEMPERATURE IN FORM OF GASES OR LIQUIDS | 2008 |
|
RU2399581C2 |
Authors
Dates
2010-01-10—Published
2008-09-24—Filed