FIELD: chemistry.
SUBSTANCE: method is realised by cold pressing under specific pressure of 12.5 MPa with subsequent saturation in engine oil M-8B at temperature 150°C for 24 hours and sintering at temperature 370±5°C. The invention enables to produce large group of cheap readily available materials with good structural and anti-frictional properties, capable of prolonged operation in self-lubrication mode in friction assemblies as friction bearings and movable sealants, including in cryogenic engineering.
EFFECT: method significantly increases wear-resistance and load capacity of articles made using the disclosed technique.
2 cl, 4 tbl, 16 ex
| Title | Year | Author | Number |
|---|---|---|---|
| BASALT-FLUOROPLASTIC COMPOSITE MATERIAL FOR TRIBOTECHNICAL PURPOSES | 2013 |
|
RU2552744C2 |
| POLYMER MATERIAL FOR TRIBOTECHNICAL PURPOSES | 2010 |
|
RU2454439C1 |
| POLYMER TRIBOTECHNICAL MATERIAL BASED ON POLYTETRAFLUOROETHYLENE, MECHANICALLY ACTIVATED KAOLIN AND MAGNESIUM SPINEL | 2019 |
|
RU2699109C1 |
| POLYMER COMPOSITE MATERIAL FOR STRUCTURAL AND TRIBOLOGICAL PURPOSES BASED ON POLYTETRAFLUOROETHYLENE AND MODIFIED SILICON DIOXIDE | 2022 |
|
RU2792599C1 |
| POLYMER MATERIAL OF TRIBOTECHNICAL PURPOSE ON THE BASIS OF POLYTETRAFLUOETHYLENE | 2018 |
|
RU2675520C1 |
| COMPOSITION THERMOSTABLE TRIBOTECHNICAL MATERIAL | 2004 |
|
RU2268273C1 |
| COMPOSITION POLYMERIC MATERIAL OF TRIBOTECHNICAL DESIGNATION | 2006 |
|
RU2319713C1 |
| POLYMER MATERIAL FOR TRIBOTECHNICAL PURPOSES | 2017 |
|
RU2664129C1 |
| TRIBOTECHNICAL-DESTINATION POLYMER COMPOSITION | 2000 |
|
RU2177963C1 |
| ANTIFRICTION FILLED COMPOSITION AND METHOD OF PREPARING SAID COMPOSITION | 2008 |
|
RU2394850C1 |