FIELD: technological processes.
SUBSTANCE: invention can be used for production of welding of steel workpiece, in particular bearing ring. When implementing butt welding is performed melting and settling to produce weld (24). Method involves stage of heat supply (22) to at least welded joint (24) of workpiece (14, 30, 32) after upsetting at welding to raise temperature of welded seam (24) or to maintain temperature of welded seam (24) at higher level. Method also includes cooling said part (14, 32, 32) to temperature exceeding temperature of martensite formation (Ms), before said stage heating (22) of workpiece (14, 30, 32) after upsetting at welding.
EFFECT: method allows avoiding or reducing formation of defects, in particular of cracks at welding of steel microstructure in zone of thermal influence near to weld corresponding microstructure of base metal.
16 cl, 7 dwg
| Title | Year | Author | Number |
|---|---|---|---|
| BEARING PART MADE BY BUTT FUSION WELDING | 2011 |
|
RU2566130C2 |
| PRODUCTION OF BEARING RACER, BEARING RACER AND BEARING | 2011 |
|
RU2570594C2 |
| METHOD OF REHEATING OF RAIL WELDING ZONE | 2012 |
|
RU2545855C1 |
| WELDED STEEL PART USED AS VEHICLE PART AND METHOD FOR MANUFACTURING SPECIFIED WELDED STEEL PART | 2018 |
|
RU2746759C1 |
| METHOD OF RESISTANCE FUSION WELDING OF STEEL RAILS | 2005 |
|
RU2296655C2 |
| METHOD OF ARE WELDING OF CIRCULAR JOINTS OF THIN-WALL SHELLS | 2008 |
|
RU2393946C2 |
| EXPLOSION-PROOF HOUSING AND METHOD OF ITS MANUFACTURING | 2018 |
|
RU2768274C2 |
| METHOD OF FLUSH-BUTT WELDING OF RAIL STEEL | 2010 |
|
RU2507045C2 |
| METHOD OF RESISTANCE FLASH-BUTT WELDING OF DIFFERENT THICKNESS PART | 0 |
|
SU990455A1 |
| BEARING RING AND PROCEDURE FOR ITS FABRICATION | 2011 |
|
RU2569171C2 |