FIELD: technological processes.
SUBSTANCE: invention relates to chemical application of metal coating of nickel-based alloys. Method involves holding articles in an aqueous solution containing components at following ratio, mol/l: nickel salt 0.075-0.125; copper salt - 0.0008-0.008, lead salt (0.6-1.2)·10-5; sodium hypophosphite 0.28-0.40; glycine 0.10-0.40; orthophosphoric acid 0.10-0.30; sodium tetraborate 0.05-0.10, wherein application of coating is performed at solution temperature 70-93 °C and pH 6.3-8.7. Salt solution used is nickel sulphate, chloride or acetate and lead salt is lead nitrate or acetate. Application of coating can be performed on surface of items made of steel, copper and alloys thereof, aluminium and alloys thereof, plastic or fibre and tissue structures from natural or synthetic materials.
EFFECT: invention ensures production of high-quality nickel-copper-phosphorus coating, containing from 5 to 8 % phosphorus and up to 8 % copper, having high lustre and intended for use as protective-decorative and protective and wear-resistant, especially after additional heat treatment.
3 cl, 1 tbl, 9 ex
Title | Year | Author | Number |
---|---|---|---|
METHOD OF CHEMICAL COATING FROM NICKEL-PHOSPHORUS ALLOY | 2015 |
|
RU2592654C1 |
METHOD OF CHEMICAL APPLICATION OF ANTIFRICTION COATING | 2018 |
|
RU2676934C1 |
METHOD FOR CHEMICAL COATING OF NICKEL-COPPER-PHOSPHORUS ALLOY | 2021 |
|
RU2756620C1 |
TECHNIQUE OF CHEMICAL PLATING MADE FROM ALLOY NICKEL-COPPER-PHOSPHORUS | 2007 |
|
RU2343222C1 |
SOLUTION FOR CHEMICAL NICKELING OF METAL PRODUCTS | 2021 |
|
RU2762733C1 |
ELECTROLYTE AND METHOD TO APPLY TIN-COBALT ALLOY COATS | 2008 |
|
RU2377344C1 |
ELECTROLYTE AND METHOD OF DEPOSITING COPPER-ZINC ALLOY COATING | 2008 |
|
RU2369668C1 |
METHOD FOR NICKEL-PHOSPHORUS COATING ELECTRODEPOSITION | 2015 |
|
RU2617470C1 |
METHOD FOR PREPARING THE SOLUTION FOR CHEMICAL NICKEL PLATING | 2020 |
|
RU2753813C1 |
COMPOSITE METAL-DIAMOND COATING, METHOD OF ITS PRODUCTION, DISPERSE SYSTEM FOR DEPOSITION OF COMPOSITE METAL-DIAMOND COATING AND METHOD FOR ITS PRODUCTION | 2019 |
|
RU2706931C1 |
Authors
Dates
2016-07-27—Published
2015-07-16—Filed