FIELD: composition of silicon-sodium-calcium type blue glass.
SUBSTANCE: proposed composition contains dyeing agents at the following ratio of components, mass-%: Fe2O3 (common iron), from 0.2 to 0.51; CoO, from 10 to 50 ppm; Cr2O3, from 10 to 300 ppm; CuO, from 0 to 400 ppm. Oxidizing-reducing coefficient of glass is lesser than or is equal to 0.35; predominant length of wave λ within 485 and 489 nm, excitation purity lesser than 13% and selectivity of at least 1.1 at thickness ranging from 3 to 5 mm. Proposed composition is used for manufacture of sheet glass for automobiles and structural glass. Light transmission of glass is 60%.
EFFECT: enhanced efficiency; improved quality.
22 cl, 4 tbl
Title | Year | Author | Number |
---|---|---|---|
BLUE GLASS AND A METHOD FOR PRODUCTION THEREOF | 2018 |
|
RU2696742C1 |
DARK-COLOURED LIME-SODA GLASS OF BLUE-GREEN SHADE | 1999 |
|
RU2329959C2 |
COMPOSITION OF GRAY GLASS OF SILICATE-SODIUM-LIME TYPE | 2001 |
|
RU2269491C2 |
COLOURED SODA-LIME GLASS | 2001 |
|
RU2327657C2 |
SODA-CALCIUM-SILICATE GLASS WITH HIGH VISIBLE LIGHT TRANSMITTANCE | 2020 |
|
RU2816148C1 |
MASKING GLASS (Versions), FLAT GLASS PLATE (Versions), CAR WINDOW BLOCK | 1998 |
|
RU2186743C2 |
HIGH LIGHT-TRANSMISSION SODA-LIME COLOR GLASS | 2001 |
|
RU2280624C2 |
SODIUM-CALCIUM GLASS WITH SKY-BLUE TONE | 1999 |
|
RU2255912C2 |
COMPOSITION OF GREY GLASS | 2006 |
|
RU2430024C2 |
GLASS COMPOSITION INTENDED FOR GLAZING, AND GLAZING | 1995 |
|
RU2145309C1 |
Authors
Dates
2007-10-10—Published
2002-12-11—Filed