FIELD: metallurgy.
SUBSTANCE: invention relates to ferrous metallurgy, in particular, to methods of protective scull forming on converter lining surface. Method consists in final slag leaving in converter, preliminary blowing of final slag with oxygen and magnesia briquetted flux addition into converter with subsequent flux modified final slag blowing with neutral gas. Between lining spraying additionally performing is magnesia briquetted flux addition in supplied into converter charging on scrap metal, wherein at each stage flux is added in amount of 2.7–8.0 kg/t of steel, spraying and melting are carried out at temperature of 1,580–1,680 °C, and used magnesia briquetted flux is composition containing magnesian component, containing periclase-carbon, in form of melting and casting units waste lining scrap and dolomite.
EFFECT: enabling increased duration of vessel campaign period from 3,000 to 5,000–8,000 melts with considerable cost-cutting of used magnesian flux.
2 cl, 2 tbl, 3 ex
Title | Year | Author | Number |
---|---|---|---|
PROCEDURE OF MELTING STEEL IN CONVERTER | 2015 |
|
RU2620217C2 |
METHOD OF APPLYING SLAG SKULL ON REFRACTORY LINING OF OXYGEN CONVERTER | 2024 |
|
RU2826359C1 |
METHOD OF MELTING METAL IN CONVERTER | 2015 |
|
RU2603759C1 |
PROCEDURE FOR COMBINED PROCESS OF CHARGE OF SLAG SCULL WITH MELTING STEEL IN CONVERTER AT REDUCED CONSUMPTION OF IRON | 2008 |
|
RU2389800C1 |
METHOD FOR APPLYING SKULL ON CONVERTER LINING | 2016 |
|
RU2632738C1 |
COVERING METHOD OF SLAG-SKIN ON VESSEL LINING | 2006 |
|
RU2342444C2 |
METHOD FOR STEEL MELTING IN CONVERTER | 2005 |
|
RU2289629C1 |
METHOD OF DEPOSITION OF THE WALL ACCRETION ON THE CONVERTER BRICK-LINING | 2005 |
|
RU2294379C1 |
METHOD FOR REPAIRING CONVERTER LINING | 2004 |
|
RU2277590C2 |
STEEL MELTING METHOD IN CONVERTER WITH COMBINED BLOWDOWN | 2019 |
|
RU2729692C1 |
Authors
Dates
2017-01-10—Published
2015-04-01—Filed