FIELD: metallurgy.
SUBSTANCE: manufacturing method of discs of gas-turbine engines from powder heat-resistant alloys on the basis of nickel is proposed and it involves obtaining of pellets, their arrangement in capsules, hot isostatic pressing, deformation, hardening and ageing. The obtained pellets are sieved into pellet with size of +10-50 mcm; hot isostatic pressing is performed at temperature of that is by 10-30°C lower than complete dissolution temperature of γ'-phase with exposure under pressure during 2-8 hours; deformation is performed by means of die forging or pressing with drawing with deformation degree of 70-90% at temperature that is by 60-100°C lower than temperature of complete dissolution of γ'-phase with further hardening against deformation temperature with speed of 50-100 degrees/min.
EFFECT: higher strength characteristics.
1 tbl, 1 ex
| Title | Year | Author | Number |
|---|---|---|---|
| MANUFACTURING METHOD OF ITEMS IN FORM OF DISCS OR ROLLS OF GAS-TURBINE ENGINES FROM PELLETISED HEAT-RESISTANT NICKEL ALLOYS | 2010 |
|
RU2433204C1 |
| HEAT TREATMENT METHOD OF DISC-TYPE PARTS OF GAS-TURBINE ENGINES FROM HEAT-RESISTANT POWDER NICKEL ALLOYS | 2010 |
|
RU2433202C1 |
| METHOD OF OBTAINING A PRODUCT OF HEAT-RESISTANT NICKEL ALLOY | 2017 |
|
RU2649103C1 |
| HEAT TREATMENT METHOD OF HEAT-RESISTANT NICKEL-BASED ALLOYS | 2010 |
|
RU2433201C1 |
| HEAT TREATMENT METHOD OF HEAT-RESISTANT POWDER NICKEL-BASED ALLOYS | 2010 |
|
RU2433203C1 |
| METHOD FOR HEAT TREATMENT OF PRODUCTS FROM HEAT-RESISTANT NICKEL ALLOY EP741NP | 2021 |
|
RU2772725C1 |
| METHOD OF PRODUCING ARTICLES FROM COMPLEX ALLOY REFRACTORY NICKEL ALLOYS | 2011 |
|
RU2457924C1 |
| METHOD FOR PRODUCTION OF PRODUCT OUT OF ALLOY TYPE "TT751¦" WITH HIGH STRENGTH AND HEAT RESISTANCE | 2011 |
|
RU2453398C1 |
| HEAT RESISTANT NICKEL ALLOY FOR PRODUCTION OF ITEMS BY METHOD OF PELLET METALLURGY | 2010 |
|
RU2428497C1 |
| METHOD TO PRODUCE PRODUCTS FROM COMPLEX-ALLOYED POWDER HEAT-RESISTANT NICKEL ALLOYS | 2012 |
|
RU2516267C1 |